Stainless steel
| Property | Units | Typical | Type 316 | Type 316L |
| Ultimate Tensile Strength | [N/mm^2] | 586 | 517.1 min | 482.6 min |
| 0.2% Offset Yield Strength | [N/mm^2] | 303.37 | 206.84 min | 172.37 min |
| Elongation in 2 inches | [%] | 56 | 40 min | 40 min |
| Reduction in Area | [%] | 69 | — | — |
| Hardness, Rockwell | [B] | 81 | 95 max | 95 max |
| Density | [Kg/m^3] | 7 888.77 | — | — |
| Modulus of Elasticity | [psi] | 29 x 10^6 | — | — |